Wholesale Aluminum foil for capacitor

Folia aluminiowa na kondensator

Stop aluminium: 1000, 3000, 8000 seriale itp
Temperatura aluminium: O - H112 itp
Szerokość: 100mm - 1600mm
Grubość: 0.0053mm - 0.2mm
Wewnętrzna średnica: 76cm, 152cm itp
Główny materiał: papier, żelazo, aluminium

Aluminum foil for capacitor parameters

Stop	Hartować	Grubość	Szerokość	Core inner diameter	Maximum outer diameter of aluminum coil	Tolerancja grubości	Zwilżalność	Brightness L
Aluminum foil for capacitors 1235	0	0.005-0.016mm	100-500mm	76	500	≦5	Class A (Test wody pędzla)	≦60

aluminum foil capacitor

The aluminum foil used in electrolytic capacitors is a corrosive material that works under polar conditions. It has higher requirements for the structure of aluminum foil. The aluminum foil used is divided into three types: cathode foil, with a thickness of 0.015mm to 0.06mm; high-voltage foil, with a thickness The thickness is 0.065mm～0.1mm, and the aluminum foil is required to be produced with high-purity aluminum; the thickness of the low-pressure foil is 0.06mm～0.1mm.

Chemical composition of high pressure raw foil and low pressure raw foil（%）
Cu(≤)	Fe(≤)	I(≤)	Glin(≥)
0.005	0.003	0.0025	99.99
0.005	0.015	0.015	99.97
0.01	0.02	0.02	99.95
0.01	0.04	0.04	99.93
0.01	0.06	0.06	99.90
0.01	0.10	0.08	99.85
0.0025~0.0050	≤0.014	≤0.014	≥99.97
Notatka: After the agreement between the supplier and the buyer, it can be supplied according to the agreement.

Chemical composition of cathode foil（%）
Cu	Fe	I	Glin
0.01	0.16	0.16	99.7
0.01	0.25	0.20	99.6
Notatka: After the agreement between the supplier and the buyer, it can be supplied according to the agreement.

Longitudinal room temperature mechanical properties of aluminum foil

Grubość (mm)	Hartować	Wytrzymałość na rozciąganie N /mm2	Wydłużenie δ %
Grubość (mm)	Hartować	not less than
0.015~0.090	M	24.5	2.0
0.015~0.090	Y	98.0	0.5
0.100~0.200	M	29.4	3.0
0.100~0.200	Y	98.0	0.5

Crystal Structure Properties of Capacitor Aluminum Foil

The average surface dislocation density of the soft-state high-pressure original foil is not more than 10∧6/cm2.
The (100) crystal plane occupancy rate of the soft-state high-pressure original foil is not less than 80%.
The thickness of the oxide film on the surface of the soft-state high-voltage original foil is not more than 6nm.

Notatka: Foils with other parameters can be supplied by agreement between the supplier and the buyer.

Aplikacja

aluminum foil for electrolytic capacitor

Dlaczego właśnie my?

Henan Huawei Aluminium Co., Sp. z o.o. jest liderem wielu producentów i dostawców aluminium w Chinach. Ściśle kontrolujemy jakość i koncentrujemy się na klientach. Mamy nadzieję nawiązać z Państwem dogłębną współpracę i zapewnić Państwu wysokiej jakości niestandardowe usługi OEM w zakresie produktów z aluminium. Jeśli chcesz uzyskać najnowsze i najlepsze ceny za kg lub za tonę wagi standardowej, proszę skontaktuj się z nami.

Linia do produkcji folii aluminiowej

Uszczelka

Pakiet: Drewniana skrzynka
Specyfikacja standardowej skrzynki drewnianej: Długość*szerokość*wysokość=1,4m*1,3m*0,8m
Raz potrzebne,Wymiary drewnianej skrzynki można przeprojektować w razie potrzeby.
Na drewnianą skrzynkę Skala masy brutto: 500-700KG Masa netto: 450-650KG
Uwaga: Do specjalnych wymagań dotyczących pakowania, odpowiednie dodaje się odpowiednio.