Aluminum foil for capacitor parameters

Slitina	Nálada	Tloušťka	Šířka	Core inner diameter	Maximum outer diameter of aluminum coil	Thickness tolerance	Smáčivost	Brightness L
Hliníková fólie pro kondenzátory 1235	0	0.005-0.016mm	100-500mm	76	500	≦5	Class A (Test kartáčovou vodou)	≦60

aluminum foil capacitor

The aluminum foil used in electrolytic capacitors is a corrosive material that works under polar conditions. It has higher requirements for the structure of aluminum foil. The aluminum foil used is divided into three types: cathode foil, with a thickness of 0.015mm to 0.06mm; high-voltage foil, with a thickness The thickness is 0.065mm～0.1mm, and the aluminum foil is required to be produced with high-purity aluminum; the thickness of the low-pressure foil is 0.06mm～0.1mm.

Chemical composition of high pressure raw foil and low pressure raw foil（%）
Cu(≤)	Fe(≤)	A(≤)	Al(≥)
0.005	0.003	0.0025	99.99
0.005	0.015	0.015	99.97
0.01	0.02	0.02	99.95
0.01	0.04	0.04	99.93
0.01	0.06	0.06	99.90
0.01	0.10	0.08	99.85
0.0025~0.0050	≤0.014	≤0.014	≥99.97
Poznámka: After the agreement between the supplier and the buyer, it can be supplied according to the agreement.

Chemical composition of cathode foil（%）
Cu	Fe	A	Al
0.01	0.16	0.16	99.7
0.01	0.25	0.20	99.6
Poznámka: After the agreement between the supplier and the buyer, it can be supplied according to the agreement.

Longitudinal room temperature mechanical properties of aluminum foil

Tloušťka (mm)	Nálada	Pevnost v tahu N /mm2	Prodloužení δ %
Tloušťka (mm)	Nálada	not less than
0.015~0.090	M	24.5	2.0
0.015~0.090	Y	98.0	0.5
0.100~0.200	M	29.4	3.0
0.100~0.200	Y	98.0	0.5

Crystal Structure Properties of Capacitor Aluminum Foil

The average surface dislocation density of the soft-state high-pressure original foil is not more than 10∧6/cm2.
The (100) crystal plane occupancy rate of the soft-state high-pressure original foil is not less than 80%.
The thickness of the oxide film on the surface of the soft-state high-voltage original foil is not more than 6nm.

Poznámka: Foils with other parameters can be supplied by agreement between the supplier and the buyer.

aplikace

aluminum foil for electrolytic capacitor

Proč nás vybrat?

Henan Huawei Aluminium Co., Ltd. je lídrem mnoha výrobců a dodavatelů hliníku v Číně. Přísně kontrolujeme kvalitu a zaměřujeme se na zákazníky. Doufáme, že s vámi budeme mít hloubkovou spolupráci a poskytneme vám vysoce kvalitní výrobky z hliníkového materiálu na zakázku OEM. Pokud chcete získat nejnovější a nejlepší ceny za kg nebo za tunu standardní hmotnosti, prosím kontaktujte nás.

Linka na výrobu hliníkových fólií

Balení

Balík: Dřevěné pouzdro
Standardní specifikace dřevěného pouzdra: Délka*Šířka*Výška=1,4m*1,3m*0,8m
Jednou potřeba,rozměr dřevěného pouzdra lze upravit podle potřeby.
Váha pro hrubou hmotnost v dřevěném pouzdře: 500-700KG Čistá hmotnost: 450-650KG
Poznámka: Pro speciální požadavky na balení, odpovídající se odpovídajícím způsobem doplní.