Wholesale Aluminum foil for capacitor

Aluminia folio por kondensilo

Al metala alojo: 1000, 3000, 8000 serio ktp
Hardita pistilo: O - H112 ktp
Larĝo: 100mm - 1600mm
Dikeco: 0.0053mm - 0.2mm
Interna diametro: 76cm, 152cm ktp
Kerna materialo: papero, fero, aluminio

Aluminum foil for capacitor parameters

Alojo	Temperaro	Dikeco	Larĝo	Kerna interna diametro	Maximum outer diameter of aluminum coil	Thickness tolerance	Malsekigebleco	Brightness L
Aluminia folio por kondensiloj 1235	0	0.005-0.016mm	100-500mm	76	500	≦5	Klaso A (Testo de broso de akvo)	≦60

aluminum foil capacitor

The aluminum foil used in electrolytic capacitors is a corrosive material that works under polar conditions. It has higher requirements for the structure of aluminum foil. The aluminum foil used is divided into three types: cathode foil, with a thickness of 0.015mm to 0.06mm; high-voltage foil, with a thickness The thickness is 0.065mm～0.1mm, and the aluminum foil is required to be produced with high-purity aluminum; the thickness of the low-pressure foil is 0.06mm～0.1mm.

Chemical composition of high pressure raw foil and low pressure raw foil（%）
Cu(≤)	Fe(≤)	Kaj(≤)	Al(≥)
0.005	0.003	0.0025	99.99
0.005	0.015	0.015	99.97
0.01	0.02	0.02	99.95
0.01	0.04	0.04	99.93
0.01	0.06	0.06	99.90
0.01	0.10	0.08	99.85
0.0025~0.0050	≤0.014	≤0.014	≥99.97
Noto: After the agreement between the supplier and the buyer, it can be supplied according to the agreement.

Chemical composition of cathode foil（%）
Cu	Fe	Kaj	Al
0.01	0.16	0.16	99.7
0.01	0.25	0.20	99.6
Noto: After the agreement between the supplier and the buyer, it can be supplied according to the agreement.

Longitudinal room temperature mechanical properties of aluminum foil

Dikeco (mm)	Temperaro	Tensila Forto N /mm2	Plilongigo δ %
Dikeco (mm)	Temperaro	not less than
0.015~0.090	M	24.5	2.0
0.015~0.090	Y	98.0	0.5
0.100~0.200	M	29.4	3.0
0.100~0.200	Y	98.0	0.5

Crystal Structure Properties of Capacitor Aluminum Foil

The average surface dislocation density of the soft-state high-pressure original foil is not more than 10∧6/cm2.
La (100) crystal plane occupancy rate of the soft-state high-pressure original foil is not less than 80%.
The thickness of the oxide film on the surface of the soft-state high-voltage original foil is not more than 6nm.

Noto: Foils with other parameters can be supplied by agreement between the supplier and the buyer.

Apliko

aluminum foil for electrolytic capacitor

Kial elekti nin?

Henan Huawei Aluminium Co., Ltd. estas la gvidanto de multaj fabrikantoj kaj provizantoj de aluminio en Ĉinio. Ni strikte kontrolas la kvaliton kaj fokusiĝas al klientoj. Ni esperas havi profundan kunlaboron kun vi kaj provizi al vi altkvalitajn aluminiajn materialajn produktojn laŭmendajn OEM-servojn. Se vi volas akiri la plej novajn kaj plej bonajn prezojn je po kg aŭ po tuno norma pezo, bonvolu kontakti nin.