Wholesale Aluminum foil for capacitor

Feuille d'aluminium pour condensateur

Alliage métallique Al: 1000, 3000, 8000 série etc.
Température de l'aluminium: O - H112 etc.
Largeur: 100millimètre - 1600millimètre
Épaisseur: 0.0053millimètre - 0.2millimètre
Diamètre intérieur: 76cm, 152cm etc.
Matériau de base: papier, fer, aluminium

Aluminum foil for capacitor parameters

Alliage	Caractère	Épaisseur	Largeur	Core inner diameter	Maximum outer diameter of aluminum coil	Tolérance d'épaisseur	Mouillabilité	Brightness L
Feuille d'aluminium pour condensateurs 1235	0	0.005-0.016millimètre	100-500millimètre	76	500	≦5	Class A (Test d'eau à la brosse)	≦60

aluminum foil capacitor

The aluminum foil used in electrolytic capacitors is a corrosive material that works under polar conditions. It has higher requirements for the structure of aluminum foil. The aluminum foil used is divided into three types: cathode foil, with a thickness of 0.015mm to 0.06mm; high-voltage foil, with a thickness The thickness is 0.065mm～0.1mm, and the aluminum foil is required to be produced with high-purity aluminum; the thickness of the low-pressure foil is 0.06mm～0.1mm.

Chemical composition of high pressure raw foil and low pressure raw foil（%）
Cu(≤)	Fe(≤)	Et(≤)	Al(≥)
0.005	0.003	0.0025	99.99
0.005	0.015	0.015	99.97
0.01	0.02	0.02	99.95
0.01	0.04	0.04	99.93
0.01	0.06	0.06	99.90
0.01	0.10	0.08	99.85
0.0025~0.0050	≤0.014	≤0.014	≥99.97
Note: After the agreement between the supplier and the buyer, it can be supplied according to the agreement.

Chemical composition of cathode foil（%）
Cu	Fe	Et	Al
0.01	0.16	0.16	99.7
0.01	0.25	0.20	99.6
Note: After the agreement between the supplier and the buyer, it can be supplied according to the agreement.

Longitudinal room temperature mechanical properties of aluminum foil

Épaisseur (millimètre)	Caractère	Résistance à la traction N /mm2	Élongation δ %
Épaisseur (millimètre)	Caractère	not less than
0.015~0.090	M	24.5	2.0
0.015~0.090	Y	98.0	0.5
0.100~0.200	M	29.4	3.0
0.100~0.200	Y	98.0	0.5

Crystal Structure Properties of Capacitor Aluminum Foil

The average surface dislocation density of the soft-state high-pressure original foil is not more than 10∧6/cm2.
Le (100) crystal plane occupancy rate of the soft-state high-pressure original foil is not less than 80%.
The thickness of the oxide film on the surface of the soft-state high-voltage original foil is not more than 6nm.

Note: Foils with other parameters can be supplied by agreement between the supplier and the buyer.

Application

aluminum foil for electrolytic capacitor

Pourquoi nous choisir?

Henan Huawei Aluminium Co., Ltd. est le leader de nombreux fabricants et fournisseurs d'aluminium en Chine. Nous contrôlons strictement la qualité et nous nous concentrons sur les clients. Nous espérons avoir une coopération approfondie avec vous et vous fournir des services OEM personnalisés de produits en aluminium de haute qualité. Si vous souhaitez obtenir les prix les plus récents et les meilleurs par kg ou par tonne de poids standard, Contactez nous s'il vous plait.

Ligne de production de feuille d'aluminium

Emballage

Emballer: Caisse en bois
Spécification standard de la caisse en bois: Longueur*Largeur*Hauteur=1.4m*1.3m*0.8m
Une fois nécessaire,la dimension de la caisse en bois pourrait être repensée au besoin.
Par caisse en bois Échelle de poids brut: 500-700KG Poids net: 450-650KG
Remarque: Pour les exigences d'emballage spéciales, correspondant doit être ajouté en conséquence.