Aluminum foil for capacitor parameters

Metalliseos	Luonne	Paksuus	Leveys	Core inner diameter	Maximum outer diameter of aluminum coil	Paksuustoleranssi	Kostuvuus	Brightness L
Aluminum foil for capacitors 1235	0	0.005-0.016mm	100-500mm	76	500	≦5	Class A (Harjavesitesti)	≦60

aluminum foil capacitor

The aluminum foil used in electrolytic capacitors is a corrosive material that works under polar conditions. It has higher requirements for the structure of aluminum foil. The aluminum foil used is divided into three types: cathode foil, with a thickness of 0.015mm to 0.06mm; high-voltage foil, with a thickness The thickness is 0.065mm～0.1mm, and the aluminum foil is required to be produced with high-purity aluminum; the thickness of the low-pressure foil is 0.06mm～0.1mm.

Chemical composition of high pressure raw foil and low pressure raw foil（%）
Cu(≤)	Fe(≤)	Ja(≤)	Al(≥)
0.005	0.003	0.0025	99.99
0.005	0.015	0.015	99.97
0.01	0.02	0.02	99.95
0.01	0.04	0.04	99.93
0.01	0.06	0.06	99.90
0.01	0.10	0.08	99.85
0.0025~0.0050	≤0.014	≤0.014	≥99.97
Huomautus: After the agreement between the supplier and the buyer, it can be supplied according to the agreement.

Chemical composition of cathode foil（%）
Cu	Fe	Ja	Al
0.01	0.16	0.16	99.7
0.01	0.25	0.20	99.6
Huomautus: After the agreement between the supplier and the buyer, it can be supplied according to the agreement.

Longitudinal room temperature mechanical properties of aluminum foil

Paksuus (mm)	Luonne	Vetolujuus N /mm2	Pidentymä δ %
Paksuus (mm)	Luonne	not less than
0.015~0.090	M	24.5	2.0
0.015~0.090	Y	98.0	0.5
0.100~0.200	M	29.4	3.0
0.100~0.200	Y	98.0	0.5

Crystal Structure Properties of Capacitor Aluminum Foil

The average surface dislocation density of the soft-state high-pressure original foil is not more than 10∧6/cm2.
The (100) crystal plane occupancy rate of the soft-state high-pressure original foil is not less than 80%.
The thickness of the oxide film on the surface of the soft-state high-voltage original foil is not more than 6nm.

Huomautus: Foils with other parameters can be supplied by agreement between the supplier and the buyer.

Sovellus

aluminum foil for electrolytic capacitor

Miksi valita meidät?

Henan Huawei Aluminium Co., Oy. on monien alumiinin valmistajien ja toimittajien johtaja Kiinassa. Valvomme tiukasti laatua ja keskitymme asiakkaisiin. Toivomme syvällistä yhteistyötä kanssasi ja tarjoamme sinulle korkealaatuisia alumiinimateriaalituotteita räätälöityjä OEM-palveluita. Jos haluat saada uusimmat ja parhaat hinnat kilolta tai tonnin vakiopainolta, ota meihin yhteyttä.