Wholesale Aluminum foil for capacitor

कॅपेसिटरसाठी ॲल्युमिनियम फॉइल

अल धातू मिश्र धातु: 1000, 3000, 8000 मालिका इ
अॅल्युमिनियम तापमान: ओ - H112 इ
रुंदी: 100मिमी - 1600मिमी
जाडी: 0.0053मिमी - 0.2मिमी
अंतर्गत व्यास: 76सेमी, 152सेमी इ
कोर साहित्य: कागद, लोखंड, अॅल्युमिनियम

Aluminum foil for capacitor parameters

मिश्रधातू	स्वभाव	जाडी	रुंदी	Core inner diameter	Maximum outer diameter of aluminum coil	Thickness tolerance	ओलेपणा	Brightness L
Aluminum foil for capacitors 1235	0	0.005-0.016मिमी	100-500मिमी	76	500	≦5	Class A (ब्रश पाण्याची चाचणी)	≦60

aluminum foil capacitor

The aluminum foil used in electrolytic capacitors is a corrosive material that works under polar conditions. It has higher requirements for the structure of aluminum foil. The aluminum foil used is divided into three types: cathode foil, with a thickness of 0.015mm to 0.06mm; high-voltage foil, with a thickness The thickness is 0.065mm～0.1mm, and the aluminum foil is required to be produced with high-purity aluminum; the thickness of the low-pressure foil is 0.06mm～0.1mm.

Chemical composition of high pressure raw foil and low pressure raw foil（%）
कु(≤)	फे(≤)	आणि(≤)	अल(≥)
0.005	0.003	0.0025	99.99
0.005	0.015	0.015	99.97
0.01	0.02	0.02	99.95
0.01	0.04	0.04	99.93
0.01	0.06	0.06	99.90
0.01	0.10	0.08	99.85
0.0025~0.0050	≤0.014	≤0.014	≥99.97
नोंद: After the agreement between the supplier and the buyer, it can be supplied according to the agreement.

Chemical composition of cathode foil（%）
कु	फे	आणि	अल
0.01	0.16	0.16	99.7
0.01	0.25	0.20	99.6
नोंद: After the agreement between the supplier and the buyer, it can be supplied according to the agreement.

Longitudinal room temperature mechanical properties of aluminum foil

जाडी (मिमी)	स्वभाव	ताणासंबंधीचा शक्ती N /mm2	वाढवणे δ %
जाडी (मिमी)	स्वभाव	not less than
0.015~0.090	M	24.5	2.0
0.015~0.090	Y	98.0	0.5
0.100~0.200	M	29.4	3.0
0.100~0.200	Y	98.0	0.5

Crystal Structure Properties of Capacitor Aluminum Foil

The average surface dislocation density of the soft-state high-pressure original foil is not more than 10∧6/cm2.
द (100) crystal plane occupancy rate of the soft-state high-pressure original foil is not less than 80%.
The thickness of the oxide film on the surface of the soft-state high-voltage original foil is not more than 6nm.

नोंद: Foils with other parameters can be supplied by agreement between the supplier and the buyer.

अर्ज

aluminum foil for electrolytic capacitor

आम्हाला का निवडा?

हेनान हुआवेई अॅल्युमिनियम कं., लि. चीनमधील अनेक अॅल्युमिनियम उत्पादक आणि पुरवठादारांचा नेता आहे. आम्ही गुणवत्ता नियंत्रित करतो आणि ग्राहकांवर लक्ष केंद्रित करतो. आम्ही तुमच्याशी सखोल सहकार्य करण्याची आणि तुम्हाला उच्च दर्जाची अॅल्युमिनियम सामग्री उत्पादने कस्टम OEM सेवा प्रदान करण्याची आशा करतो. तुम्हाला प्रति किलो किंवा प्रति टन मानक वजनानुसार नवीन आणि सर्वोत्तम किंमती मिळवायच्या असतील, कृपया आमच्याशी संपर्क साधा.