Wholesale Aluminum foil for capacitor

Aluminiumsfolie for kondensator

Al metalllegering: 1000, 3000, 8000 serie osv
Aluminium temp: O - H112 osv
Bredde: 100mm - 1600mm
Tykkelse: 0.0053mm - 0.2mm
Indre diameter: 76cm, 152cm osv
Kjernemateriale: papir, jern, aluminium

Aluminum foil for capacitor parameters

Legering	Temperament	Tykkelse	Bredde	Kjerne indre diameter	Maximum outer diameter of aluminum coil	Tykkelsestoleranse	Fuktbarhet	Brightness L
Aluminiumsfolie for kondensatorer 1235	0	0.005-0.016mm	100-500mm	76	500	≦5	Klasse A (Test av børstevann)	≦60

aluminum foil capacitor

The aluminum foil used in electrolytic capacitors is a corrosive material that works under polar conditions. It has higher requirements for the structure of aluminum foil. The aluminum foil used is divided into three types: cathode foil, with a thickness of 0.015mm to 0.06mm; high-voltage foil, with a thickness The thickness is 0.065mm～0.1mm, and the aluminum foil is required to be produced with high-purity aluminum; the thickness of the low-pressure foil is 0.06mm～0.1mm.

Chemical composition of high pressure raw foil and low pressure raw foil（%）
Cu(≤)	Fe(≤)	Og(≤)	Al(≥)
0.005	0.003	0.0025	99.99
0.005	0.015	0.015	99.97
0.01	0.02	0.02	99.95
0.01	0.04	0.04	99.93
0.01	0.06	0.06	99.90
0.01	0.10	0.08	99.85
0.0025~0.0050	≤0.014	≤0.014	≥99.97
Merk: After the agreement between the supplier and the buyer, it can be supplied according to the agreement.

Chemical composition of cathode foil（%）
Cu	Fe	Og	Al
0.01	0.16	0.16	99.7
0.01	0.25	0.20	99.6
Merk: After the agreement between the supplier and the buyer, it can be supplied according to the agreement.

Longitudinal room temperature mechanical properties of aluminum foil

Tykkelse (mm)	Temperament	Strekkstyrke N /mm2	Forlengelse δ %
Tykkelse (mm)	Temperament	not less than
0.015~0.090	M	24.5	2.0
0.015~0.090	Y	98.0	0.5
0.100~0.200	M	29.4	3.0
0.100~0.200	Y	98.0	0.5

Crystal Structure Properties of Capacitor Aluminum Foil

The average surface dislocation density of the soft-state high-pressure original foil is not more than 10∧6/cm2.
De (100) crystal plane occupancy rate of the soft-state high-pressure original foil is not less than 80%.
The thickness of the oxide film on the surface of the soft-state high-voltage original foil is not more than 6nm.

Merk: Foils with other parameters can be supplied by agreement between the supplier and the buyer.

applikasjon

aluminum foil for electrolytic capacitor

Hvorfor velge oss?

Henan Huawei Aluminium Co., Ltd. er leder for mange aluminiumsprodusenter og leverandører i Kina. Vi kontrollerer strengt kvaliteten og fokuserer på kundene. Vi håper å ha et dyptgående samarbeid med deg og gi deg høykvalitets aluminiumsmaterialprodukter tilpassede OEM-tjenester. Hvis du ønsker å få de nyeste og beste prisene per kg eller per tonn standardvekt, værsåsnill kontakt oss.