5052 Aluminum VS 6061 Aluminum

5052 Aluminum VS 6061 Aluminum

Differences Between Aluminum 5052 And Aluminum 6061

5052-aluminum-vs-6061
5052-aluminum-vs-6061

Introduction of 5052 aluminum alloy

Aluminum 5052 is the most widely used aluminum alloy in the 5000 series. 5052 aluminum belongs to the A1-Mg alloy, also known as rust-proof aluminum. 5052 aluminum alloy has high strength. When magnesium is added, 5052 aluminum plate has better corrosion resistance and enhanced strength. Aluminum alloy 5052 with excellent properties can be widely used to manufacture aircraft fuel tanks, oil pipes, sheet metal parts of transportation vehicles and ships, instruments, street lamp brackets and rivets, hardware products, electrical-appliance housings, etc.

What is 6061 grade aluminum alloy?

6061 aluminum is a heat-treatable alloy in the 6xxx series. Aluminum 6061 has good formability, weldability, and machinability. It also has medium strength and can maintain good strength after annealing. A small amount of copper or zinc can be added to 6061 aluminum alloy to improve the strength of the alloy without significantly reducing its corrosion resistance;

5052 aluminum vs 6061 element content

Chemical composition of 6061 aluminum alloy

6061 aluminum alloy chemical composition
Elements Si Fe Cu Mn Mg Cr Zn Ti Al
Content(%) 0.4-0.8 0.7 0.15-0.40 0.15 0.8-1.2 0.04-0.35 0.25 0.15 Remain

Chemical composition of 5052 aluminum alloy

5052 aluminum alloy chemical composition
Elements Si Cu Mg Zn Mn Cr Fe Others Al
Content(%) ≤0.25 ≤0.10 2.2-2.8  ≤0.10  ≤0.10 0.15-0.35 0.05 ≤0.15 Remain

Comparison of mechanical properties of aluminum alloys 5052 and 6061

Aluminum 5052 and 6061 are both aluminum metals with high strength, and there are great similarities in mechanical properties.

Property 5052 Aluminum Alloy 6061 Aluminum Alloy
Ultimate Tensile Strength 193 – 228 MPa (28 – 33 ksi) 241 – 310 MPa (35 – 45 ksi)
Yield Strength 89 – 131 MPa (13 – 19 ksi) 145 – 276 MPa (21 – 40 ksi)
Elongation at Break 12% – 20% 8% – 17%
Brinell Hardness 60 95
Shear Strength 138 MPa (20 ksi) 207 MPa (30 ksi)
Fatigue Strength 68 MPa (10 ksi) 96 MPa (14 ksi)

5052 aluminum vs 6061 density

6061 aluminum vs 5052 density aluminum lb/in³ aluminum density kg/m³
density of 6061 aluminum 0.098 2700
aluminum 5052 density 0.097 2680