Aluminium ke hore 99% e hloekileng kapa e phahameng e bitsoa aluminium e hloekileng. Aluminium ea mantlha, tšepe e hlahisoang ka seboping sa electrolysis, e na le letoto la “litšila”. Leha ho le joalo, ka kakaretso, ho feta feela likarolo tsa tšepe le silicon 0.01%.
Bakeng sa foil kholo ho feta 0.030 mm (30µm), motsoako o tloaelehileng oa aluminium ke en aw-1050: foil e hloekileng ea aluminium e nang le bonyane 99.5% aluminium. (Aluminum larger than 0.300mm is usually called aluminum strip or aluminum plate.).
Aluminium foil is usually pure aluminum (99–99.9% aluminum content). The so-called pre-rolled strip is approx. Aluminum foil with a thickness of 0.6–1.5 mm is cold rolled to the desired thickness in several rolling steps (passes).
When producing very thin foils, two layers are rolled. This has two different surfaces (glossy and matt). The reason is that the outer surface is in contact with the polishing machine and thus becomes relatively smooth (glossy). Ka papiso, the inner surface is slightly rough due to free-forming, so due to strong forming, the aluminum hardens during rolling, which means that the aluminum becomes more and more the harder. Subsequent soft annealing makes it soft and flexible again.
Botenya: 10μm(0.010mm),15μm(0.015mm),20μm(0.020mm),30μm(0.030mm),50μm(0.050mm),100μm(0.100mm),150μm(0.150mm),200μm(0.200mm),300μm(0.300mm).
Bophara: 1.0mm,1.2mm,1.25mm,500mm.
Bolelele: 5m,10m,25m,50m,100m,150m,200m,250m.
Henan Huawei Aluminium Co., Ltd. ke moetapele oa lihlahisoa tse ngata tsa aluminium le barekisi ba China. Re laola ka thata boleng le ho tsepamisa maikutlo ho bareki. Re tšepa ho ba le tšebelisano-'moho e tebileng le uena le ho u fa litšebeletso tsa boleng bo holimo tsa lihlahisoa tsa aluminium tsa tloaelo tsa OEM. Haeba u batla ho fumana litheko tse ncha ka ho fetesisa ka k'hilograma kapa boima ba boima ba lithane, ka kopo ikopanye le rona.